Mineral plaster imitating the natural wood texture. A mixture of white cement and lime, quartz flour and selected dolomite aggregates as well as modifying additives and a hydrophobizer.

Features

• high strength and durability - thanks to the use of a polymerized cement-lime mortar based on white cement and a hydrophobizer ensuring high structural tightness of the expedition
• high alkalinity of the plaster coating and hydrophobization constitute a natural protection against the development of fungus in the decomposition of mold and algae - this applies especially to the site in the nearby green areas and water reservoirs, in shaded places in city centers with a high concentration of pollutants
• high resistance to the formation of microcracks - through the use of a specially selected bulk pile, fine fillers and additional structural reinforcement in the form of microfibers
• Does not attract dust, dirt and pollen in airborne
• color and texture - white, imitating wood (after pressing the silicone form)
• aggregate thickness - up to 1.0 mm
• possibility of machine application by means of a plastering unit
• highly breathable
• waterproof
• frost-resistant
• outside

Application

• place of use: facade in the thermal insulation system with polystyrene, facade in the thermal insulation system with mineral wool, single-layer wall elevation
• types of object in: housing construction; public utility, educational, office and healthcare facilities; commercial and service construction; passive construction, energy-saving construction
• location of the object: urban and urban areas, industrial areas, investment areas and economic zones, rural and agricultural areas + wetlands and humid areas, water reservoirs, in the vicinity of trees and green areas, shaded areas
• type of substrate: reinforced layers of the indicated thermal insulation system, concrete, traditional, cement and cement-lime plasters, made on brick walls, ceramic, cellular or silicate blocks and blocks

Technical data

• diffusion depending on the thickness of the air layer 0.14 m <Sd <1.4 m
• water vapor permeability - category V ₂ - medium (with stain)
• water permeability ≤ 1 ml / cm ² after 48 h (after the required seasoning cycles)
• pH 12
• mixing ratio water / dry mortar 0.21-0.24 l / 1 kg, 5.25-6.0 l / 25 kg
• temperature of use (substrate and environment) from +5 C to +30 C
• mortar readiness time 1.0 h
• stain painting 3 days
• fire reaction class A1
• water absorption W _c 1
• water permeability after required seasoning cycles ≤ 1 ml / cm ² after 48 h
• water vapor permeability μ ≤ 30
• adhesion after the required seasoning cycles 0.3 N / mm - FP: B
• average consumption about 2.5-3.0 kg of plaster per 1 m ²
• package 25 kg