A mixture of hydraulic binders, selected aggregates as well as modifying additives and a hydrophobizer with high resistance to microcracking.

Features

• high durability of the expedition during operation - thanks to the addition of redispersible polymer in, microfibers and special additives and modifiers in
• resistance to the effects of atmospheric agents and UV radiation
• additional improvement of the strength parameters of the plaster during its use, obtained thanks to the positive effect of the natural carbonation process of the plaster in mineral, which contributes to reducing water absorption, hardening the structure, increasing resistance to chemical aggression
• high resistance to the formation of micro-cracks - thanks to a specially selected bulk pile of fine fillers and additional structural reinforcement using microfibers
• exceptional care for the natural environment at the production stage, taking into account the requirements of sustainable development, is confirmed by the Type III Environmental Declaration
• resistance to the development of microorganisms in
• highly breathable
• smooth color and texture, imitating architectural concrete
• freedom to create an invoice
• aggregate thickness up to 1.5 mm

Application

• place of use: facade in the thermal insulation system with polystyrene; façade in a thermal insulation system with mineral wool; single-layer wall facade
• types of object in: housing construction; public utility, educational, office and healthcare facilities; commercial and service construction; historic buildings; passive construction; energy-efficient construction
• location of the object: urban and urban areas; industrial, investment and economic zones; rural and agricultural areas; wet and wet areas, water reservoirs around; close proximity to a tree stand and a green area; shady places
• types of substrate: reinforced layers of the indicated thermal insulation system; concrete; traditional, cement and cement-lime plasters on walls made of bricks, blocks and blocks in ceramic, cellular or silicate

The product is intended for making surfaces imitating the texture of concrete and the structure of drawn plaster - it creates a durable and decorative finish of the facade surface. It can be used on the entire surface of the façade cut by peaks or its fragments. It is intended for decorative and protective thin-layer plastering:

• in complex systems of thermal insulation of external walls of a building with the use of polystyrene boards (EPS) and mineral wool
• on different, properly prepared mineral substrates (e.g. concrete, traditional cement and cement-lime plasters)

Technical data

• mixing ratio: water / dry mortar 0.24-0.26 l / 1 kg, 6.0-6.5 l / 25 kg
• temperature of use (substrate and environment) from +5 C to + 25 C
• mortar readiness time approx. 3 h *
• maturing time about 5 minutes *
• protection with impregnation for 3 days (this period may be extended depending on weather conditions)
• diffusion resistance 0.14 m <Sd <1.4 m
• pH 12
• reaction to fire A1
• water absorption W _C 1
• water permeability after seasoning cycles ≤ 1 ml / cm ² after 48 h
• water vapor permeability μ ≤ 30
• adhesion after the required seasoning cycles 0.3 N / mm - FP: B
• average consumption <3.0 kg of plaster per 1 m ²
• package 25 kg

* applies to +20 C temperature and 50% air humidity