It is used for gluing foamed polystyrene boards to typical mineral substrates and making a layer reinforced with foamed fiberglass mesh. It is used when insulating external walls of buildings in the technology of seamless thermal insulation system. It is also used for leveling (unevenness up to 5 mm) and smoothing mineral substrates before applying paint and thin-layer plaster. The product properties allow application in reduced ambient temperature ranges, i.e. from 0 C, and after 8 hours. since application, possible temperature drops to -5 C.

Technical data

• Mixing proportions: 5.25-5.75 l water per 25 kg of glue
• Open work time: approx. 1.5 hours
• Flow: <0.12 mm
• Adhesion:
  • adhesion to concrete:> 0.6 MPa
  • for foamed polystyrene:> 0.1 MPa (tear in the foamed polystyrene layer)
• Consistency: dry powder
• Shelf life: under appropriate conditions, up to 12 months from the date of production
• all technical specifications are given for a relative humidity of 60% and an air temperature of +20 ° C
• Consumption of adhesive mortar when insulating the building:
• when bonding foamed polystyrene boards on a properly prepared base, it is approx. 4.0 kg / m2 when making the reinforced layer is approx. 4.0 kg / m2
• When filling the substrate with BOLIX UZ adhesive mortar, its consumption depends on the thickness of the layer produced and is on average 1.3 kg / m2 (dry adhesive) for every 1 mm of layer thickness. In order to accurately determine the product consumption on a given substrate, it is recommended to carry out appropriate tests.
• composition: BOLIX UZ glue is a dry mix of hydraulic binders, polymer, base of fine-grained mineral fillers and modifying additives.