It is used to level and fill unevenness in mineral substrates before making thin-layer plaster, fastening thermal insulation boards in thermal insulation systems, laying ceramic and stone cladding and pouring self-leveling floor mortars (on a cement or anhydrite basis). It is used outside and inside the building (including also in rooms exposed to temporary moisture), on non-deformable concrete, anhydrite substrates, on ceramic brick walls, sand-lime brick, cellular concrete as well as on cement and cement-lime plaster coatings . BOLIX W mortar is also used for masonry with a block and a component of cellular concrete

Technical data

• Mixing proportions: 2.75 3.25 l of water per 25 kg of mortar
• Compressive strength (after 28 days):> 8 MPa
• Flexural strength (after 28 days):> 3 MPa
• The load caused by walking layers of thickness 15 mm: after 24 hours
• Full load: after 14 days
• Consistency: dry powder
• Shelf life: under appropriate conditions, up to 12 months from the date of production
• Moisture resistance: periodically resistant
• Aging resistance: resistant
• Oil and solvent resistance: not resistant
• Acid and alkali resistance: not resistant
• Temperature resistance: from -20 C to +50 C
• all technical data are provided for a relative humidity of 60% and an air temperature of +20 C /
• The average consumption of adhesive mortar for making the dressing layer on a properly prepared substrate is approx. 1.90 kg / m2 for every 1 mm of layer thickness. In order to determine the exact consumption of the product, it is recommended to carry out tests on a given surface.
• composition: BOLIX W mortar is a dry mixture of hydraulic binders, polymer, base of fine-grained mineral fillers and modifying additives.