Epoxy paint, two-component, mass-dyed, water-dispersed, used to protect mineral surfaces.

Features

• high abrasion resistance
• vapor permeable
• increases the chemical resistance of substrates
• easy to apply
• solvent free
• for use on slightly moist substrates

Application

The paint is intended for coating protection of mineral substrates such as cement mortar, self-leveling mass, concrete, mineral screed, etc. It is used in places where mechanical loads occur due to forklifts and other vehicles with rubber tires, pedestrian traffic. Due to its vapor permeability, it can be used in rooms exposed to permanent moisture, e.g. in cellars, where the ground humidity does not exceed 6%. It is suitable for making durable, aesthetic and easy-to-clean floors in multi-level car parks, garages, warehouses, technical rooms and industrial halls. The product can be used inside buildings. The consistency of the paint allows it to be used on ceilings and vertical surfaces.

Technical data

• epoxy resin base
• basic colors gray RAL 7040, on special request gray-beige (RAL 7032) and beige (RAL 1015)
• density at +20 C (A + B) 1.32 g / cm ³
• mixing ratio 100 parts by weight of component A to 24 parts by weight of component B
• application temperature from +12 C to +30 C
• working time after mixing the component in about 30 minutes at the temperature of +20 C
• drying time to the 3rd degree of drying in a thin layer 7 hours at a temperature of +20 C
• application of the next layer after 12 h at the temperature of +20 C
• pedestrian traffic after 24 hours at a temperature of +20 C
• full operational parameters after about 6 days
• capillary absorption and water permeability of 0.0285 kg / (m ² xh ^0.5); in relation to the limit value W <0.1 kg / (m ² xh ^0.5 ) (according to PN-EN 1504-2)
• scratch resistance after 6 days (Clemen apparatus) 250
• coating resistance to impact class I ≥ 4 Nm (according to PN-EN 1504-2)
• abrasion resistance, Taber method 291.4 mg in relation to the limit value of 3000 mg (according to PN-EN 1504-2)
• coating adhesion when tearing off 4.6 MPa, cohesive failure in concrete 100% in relation to the limit value of 1.5 MPa (according to PN-EN 1504-2)
• reaction to fire class B _fl –s1
• product b in accordance with PN-EN 1504-2: 2006
• consumption: primer from 0.15 kg / m ² to 0.30 kg / m ² ; sealing layer from 0.20 kg / m ² to 0.50 kg / m ²
• packaging 15 kg set (component A + B)