A two-component product based on epoxy, solvent free, medium viscosity and low reactivity. Especially recommended for renovation works in wooden structures, consisting in filling the space and fixing the rod in.

Features

• very good adhesion to wooden substrates
• high mechanical strength, no shrinkage, ability to withstand multiple loads and vibrations
• the product's low elasticity coefficient, making it particularly compatible with wooden structures
• good chemical resistance to oils, fats, fuels, diluted acids and alkaline solutions
• after hardening, the product is waterproof
• non-toxic material, solvent-free, non-flammable, suitable for use in poorly ventilated rooms

Application

• consolidation and reconstruction of the fragment and reconstruction of damages in wooden beams
• repair of damaged wooden beams by replacing or joining boards, sections and wooden elements
• joining wooden joints, panels and vertical structures made of wood
• recreating the mechanical properties of wooden structures of high architectural, historical or decorative value
• fastening and anchoring in wooden structures v

Technical data

• external appearance and color of the mixture (A + B) translucent liquid
• mixing ratio component in A: B (by weight) 3.15: 1.85
• binder-aggregate mixing ratio (by weight) from 1: 2 to 1: 6
• application temperature 10-30 C
• shelf life at temperatures of 10 C / 20 C / 30 C: 4-5 / 1 / h
• total setting time at 20 ° C - 5 days
• pure epoxy density at 20 C - 1.1 g / cm ³
• the density of the mixture of epoxy with aggregate in the proportion of 1: 5 at a temperature of 20 C - 2.0 g / cm ³
• modulus of elasticity of pure epoxy 30,000 kp / cm ²
• modulus of elasticity of the mixture of epoxy with aggregate in the proportion 1: 5 - 60,000 kg / cm ²
• compressive strength of pure epoxy 700 kp / cm ²
• compressive strength of the epoxy-aggregate mixture in the proportion of 1: 5 800 kp / cm ²
• bending strength of pure epoxy 300 kp / cm ²
• flexural strength of the mixture of epoxy with aggregate in the proportion 1: 5 350 kp / cm ²
• excellent water resistance
• chemical resistance excellent
• consumption 1.1 pure epoxy (kg / m 1 mm of thickness)
• consumption of the mixture of epoxy with aggregate in the proportion of 1: 5 2.0 (kg / m 1 mm of thickness)
• package 5 kg