A flexible, one-component, polyurethane based sealant that matures on contact with ambient moisture. By applying this material, we obtain a strong and very elastic seal in a wide temperature range.

Features

• ready-to-use sealant; does not require additional mixing on site
• it has excellent adhesion to construction materials such as concrete and brick; natural stone; glass; wood; steel; metal

Application

Used to fill expansion joints with certain movements, construction joints, wherever permanent elastic filling is required, e.g .:

• as a filling material for expansion joints in floors
• as a filling material for dilatations in water reservoirs and sewage treatment plants wastewater in - in connections element in prefabricated (large slab)
• for sealing doors and windows
• in sealing roof panels
• when sealing the balcony and terrace in

Technical data

• density 1.3 g / cm ³
• application and maturation temperature + 5 ° C to + 40 ° C
• film formation at 23 C and 50% humidity 60-100 min
• hardening for 24 h at 23 C and 50% relative humidity 3 mm
• movement of expansion joints during use 25%
• tensile strength 0.40 MPa
• 100% elongation tensile strength (MPa) 0.46 MPa
• elongation at break 80%
• compressibility 80%
• Shore A hardness 40
• temperature range during use from 20 C to + 80 C
• resistance to action: aqueous solution with SO ₄ ion content from 2 to 6000 mg / l '; an aqueous solution with an ion content in NH ₄ + up to 100 mg / l; an aqueous solution with an ion content in Mg2 + up to 3000 mg / l; aqueous solution in hydrochloric acid at a concentration of up to 1%; aqueous phenol solution up to a concentration of 1%; Kit Maxflex 100 LM is resistant to the occasional effect of an aqueous solution in sodium hypochlorite with a concentration of up to 1%
• consumption - 100 ml is needed to fill 1 running meter of a 10x10 mm joint
• package: sausage 0.6 l, carton of 20 pieces