A water-based, three-component polyurethane-cement mortar, intended for trowel application in layers of 4-15 mm. On the floor, it creates a continuous anti-slip coating characterized by a delicate texture and high resistance to abrasion, impact, rapid temperature changes and chemical impact.

Features

• thermal resistance higher than epoxy coatings from -40 C to +150 C
• a coating over 9 mm thick is not affected by the steam cleaning cycles
• high mechanical parameters, great compressive strength, abrasion, impact strength, mechanical cleaning, etc.
• excellent chemical resistance, better than epoxy system
• product suitable for use on slightly damp surfaces and on fresh concrete (7 days after pouring)
• application possible in layers of different thickness depending on the needs and requirements
• the finishing layer may have a different texture depending on the planned anti-skid properties
• creates an uninterrupted coating without structural joints
• quick-drying material: moderate traffic is possible after 24 hours from application
• environmentally friendly product, non-toxic, solvent-free, non-flammable, suitable for use in rooms with low air movement

Application

• floor systems exposed to rapid temperature changes, steam cleaning cycles or splashes of hot liquids, for industrial environments with high operating conditions, for cold rooms, etc.
• anti-slip coating for floors exposed to direct contact with liquids, for surfaces where liquids are loaded and unloaded, for surfaces with a slight slope on which forklifts travel, etc.
• in industrial environments on substrates requiring high mechanical strength and chemical resistance to cleaning substances, degreasing surfactants, acid and alkaline solutions, hydrocarbons and other aggressive substances
• industrial floors in the petrochemical, pharmaceutical, food, etc. industries, which impose very high requirements on the materials used in terms of mechanical and chemical resistance

Technical data

• component density in A / B / C 0.99 / 1.23 / 1.50 0.10 g / cm ³
• density of A + B + C fresh mix 2.05 0.10 g / cm ³
• density of the mature product and after drying 2.00 0.10 g / cm ³
• minimum application temperature of substrate and surroundings> 5 ° C
• pot life at 20 ° C 20 min
• initial / final setting time at 20 ° C 1-2 / 3-4 h
• complete solidification time at 20 ° C and 50% relative humidity before putting into service for: pedestrian traffic 12 days; moderate vehicular traffic 24 days; heavy traffic 48 days
• compressive strength after 28 days> 40 N / mm ² (according to EN 13892-2)
• bending strength after 28 days> 10 N / mm ² (according to EN 13892-2)
• adhesion to concrete after 28 days> 3 N / mm ² (according to EN 13892-8) (concrete breaking)
• thermal resistance of a layer ≥ 4.0 mm thick from -15 C to +60 C; ≥ 6.0 mm from -25 C to +70 C; ≥ 9.0 mm from -40 C to +120 C; ≥ 12.0 mm from -40 C to +130 C (occasionally up to +150 C)
• minimum / maximum thickness of one layer 4/15 mm
• consumption * per one layer 2.0 kg / m mm
• packaging: a set of 31.44 kg