Solvent-free, two-component epoxy binder recommended for floor systems with high mechanical and chemical properties for the protection and decorative finish of concrete and mortar.

Features

• due to its high abrasion resistance, it is suitable for heavy vehicular traffic
• very good resistance to chemicals: oils, greases, gasoline, acids and alkaline solutions, solvents, salts, etc.
• very good adhesion to concrete and mortar
• provides a continuous, uniform and consistent surface, with a non-slip finish
• easy to clean and maintain
• wide range of applications
• non-toxic, solvent-free and non-flammable
• quick maturation and putting into service

Application

• high abrasion resistance of the coating
• anti-skid multi-layer system with aggregate
• self-leveling system with high mechanical and chemical properties in garages, warehouses, sports halls, etc.

Technical data

• appearance and color of component A colored, homogeneous paste
• the appearance and color of component B is a clear, yellowish liquid
• Component ratio in A: B (weight) 4: 1
• component w proportions for A + B: C self-leveling mortar (to the weight) 1: 1 component w proportions for a dry mortar A + B: C (to the weight) 1: 3
• solids content component in A + B + C 100%
• component density in A + B 1.45 0.1 g / cm ³
• density for self-leveling mortar / dry mortar 1.90 / 2 0.1 g / cm ³
• flammability of the product non-flammable
• application and maturation temperature T / RH 8-30 C /> 85%
• shelf life at 10 C / 20 C / 30 C - 45/30/10 min
• drying time at 20 C 6–8 h
• time between the planes at 20 ° C 6-24 h
• maturing time at 20 ° C: 1 days for pedestrian traffic; for high beam 3 days; for heavy vehicle traffic 4 days
• bending strength for 28 days 32.6 MPa (according to EN 13892-2)
• compressive strength for 28 days 61.0 MPa (according to EN 13892-2)
• adhesion to concrete for 28 days> 3 MPa (according to EN 13892-2)
• consumption / thickness: applied as a clean surface - consumption for one coat / total application 0.25-0.3 / 0.5-0.6 kg / m ² ; - thickness per coat / total application 170–200 / 340–400 kg / m ² ; applied as an emitted multilayer system - total estimated consumption for resin A + B / aggregate C 1.0–1.2 / 1.0–1.5 kg / m ² - recommended thickness 1–2 mm; applied as a self-leveling mortar - expected consumption 2.0 kg / m ² mm of thickness - recommended thickness for a layer 1–2 mm; applied as a dry mortar: consumption 2.0 kg / m ² mm of thickness - recommended thickness for a layer of 2-10 mm
• package 25 kg