Sika - SikaRepair -13F betono remonto skiedinys
kaina pagal užklausimą
kainoraščio kaina
vieneto grynasis
0.79EUR už kg
reklaminė kaina
vieneto grynasis
0.72EUR už kg
minimalus komercinis
produkto kiekis
25.00 kg
visos kainos
grynasis kainoraštis
19.81EUR
už 25.00 kg
visos kainos
reklaminis tinklas
18.06EUR
už 25.00 kg
kainoraščio kaina
bruto vienetas 0.97EUR
už kg
reklaminė kaina
bruto vienetas
0.89EUR
už kg
minimalus komercinis
produkto kiekis
25.00 kg
visos kainos
kainoraštis bruto
24.36EUR
už 25.00 kg
visos kainos
reklaminė bruto
22.21EUR
už 25.00 kg
Produkto aprašymas
One-component polymer-cement mortar (PCC), containing microsilica, reinforced with synthetic fibers. The product is a repair mortar for filling concrete defects with the Sika Repair-10 F bonding coat. The mortar can be applied by hand or by wet spraying.
Features
- material supplied ready for use, requires mixing only with water
- ease of preparation and application
- resistance to chemical aggression
- class R4 in accordance with PN-EN 1504-3
- good mechanical properties, tightness
Application
- structural and non-structural repairs by manual method concrete in areas exposed to increased environmental aggression, e.g. in general construction, hydrotechnical construction: dams, reservoirs, canals, dams, sewage treatment plants; by industry: pavements, underground workings, shafts
- suitable for repair works (principle 3, methods 3.1 and 3.2 of PN-EN 1504-9) - repairing peeled or damaged concrete in buildings and other reinforced concrete structures (manual application of repair mortar, application of a mortar layer)
- suitable for structural reinforcement (principle 4, method 4.4 of PN-EN 1504-9) - increasing the load-bearing capacity of the concrete structure by adding a mortar layer
- suitable for maintaining or restoring passivity (principle 7, method 7.1 and 7.2 of PN-EN 1504-9) - increasing the thickness of the reinforcement cover and replacing damaged or carbonated concrete
- in the Sika Repair F concrete repair system, local filling the defect in 1-4 cm thick layers on the Sika Repair-10 F bonding layer
Technical data
- chemical base cement, polymer, microsilica, synthetic fibers, selected aggregate, special additives
- appearance / color gray powder
- density ~ 2.06 kg / dm 3 (density of hardened mortar after 28 days)
- maximum grain size D max 4 mm
- content of soluble ions in chloride ≤ 0.05% (according to PN-EN 1015-17)
- compressive strength ≥ 45 MPa, class R4; 28 days: ~ 54 MPa (according to PN-EN 12190)
- modulus of elasticity in compression ~ 27 GPa (according to PN-EN 13412)
- peel strength ~ 2.7 MPa tests with Sika Repair-10 F bonding layer (according to PN-EN 1542)
- thermal compatibility part 1: freeze-thaw ~ 2.4 MPa tests with Sika Repair-10 F bonding layer (according to PN-EN 13687-1)
- reaction to fire class A1 (according to PN-EN 13501-1)
- capillary absorption ≤ 0.5 kg m -2 h -0.5 (according to PN-EN 13057)
- Corrosion test meets (according to PN-EN 13295)
- Sika Repair-13 F mixing ratio: water - 100: 12 by weight - 3 liters of water per 25 kg bag
- theoretical consumption ~ 19.5 kg / m 2 / cm
- layer thickness minimum 1 cm / maximum 4 cm in one laying cycle
- application conditions ambient and substrate temperature min. +5 C / max. +30 C
- suitability for use ~ 60 min (at a temperature of +20 C)
- storage conditions: store in a dry room, in closed and undamaged packages; protect from moisture; best to use within 6 months from the production date
- package 25 kg bag
Techniniai duomenys - savybės
priedai